ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
AO-20 | 27676-62-6 | White powder M.P.220-222℃ M.W.784 |
Excellent resistance to discoloration. Low volatility and excellent retention in the polymer. |
AO-30 | 1843-03-4 | White powder M.P. 183-185℃ M.W.545 |
Highly efficient radical scavenger due to sterically-less-hindered structure. Excellent resistance to extraction. For polymers which contain unsaturated bonds such as ABS and elastomers. |
AO-40 | 85-60-9 | White powder M.P. 210-214℃ M.W.383 |
Highly efficient radical scavenger due to sterically-less-hindered structure. Good compatibility with many polymers. For polymers which contain unsaturated bonds such as ABS and elastomers. |
AO-50 | 2082-79-3 | White powder White flake M.P. 51-54℃ M.W.531 |
Excellent compatibility with many polymers. Excellent resistance to discoloration. |
AO-60 | 6683-19-8 | White powder White granule M.P. 110-130℃ M.W.1178 |
Very low volatility and excellent resistance to extraction due to high M.W. Excellent processing and long-term heat stabilization. |
AO-80 | 90498-90-1 | White powder M.P. 110-120℃ M.W.741 |
Highly efficient radical scavenger Exceptional processing and long-term heat stabilization Excellent resistance to discoloration, particularly against NOx gas. |
AO-330 | 1709-70-2 | White powder M.P. 243-245℃ M.W.775 |
Low volatility Excellent resistance to extraction from the polymer, particularly in hot water. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
PEP-8 | 3806-34-6 | White flake Softening point 50-62℃ M.W.733 |
Reduces discoloration effectively during processing. For polymers which are easy to discolor. |
PEP-36 | 80693-00-1 | White powder M.P.234-240℃ M.W.633 |
Exceptional process stability. Reduces discoloration effectively during processing. For polymers which need high-temperature processing and/or severe color stability. |
HP-10 | 126050-54-2 | White powder M.P.146-152℃ M.W.583 |
Excellent process stability. Excellent compatibility with low-polar polymers such as PE and elastomers. |
2112 | 31570-04-4 | White powder White granule M.P.180-190℃ M.W.647 |
Generic phosphite with the highest resistance to hydrolysis among commercial phosphites. |
C | 15647-08-2 | Clear liquid Vis. 10mPaㆍs M.W.346 |
Generic alkylarylphosphite. For PS, elastomers, etc. |
135A | 26544-23-0 | Clear liquid Vis. 15mPaㆍs M.W.375 |
Generic alkylarylphosphite. For PS, elastomers, etc.s |
3010 | 25448-25-3 | Clear liquid Vis. 20mPaㆍs M.W.503 |
Trialkylphosphite. Resistance to discoloration during/after processing. For polymers which require high-temperature processing. |
TPP | 101-02-0 | Clear liquid Vis. 18mPaㆍs M.W.310 |
Generic arylphosphite. Resistance to discoloration during/after processing. For PS, PU, elastomers, etc. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
AO-412S | 29598-76-3 | White powder M.P.46-52℃ M.W.1,162 |
Excellent long-term heat stability compared to DLTDP or DSTDP Very low volatility. Excellent resistance to extraction. |
AO-503 | 10595-72-9 | Clear liquid Vis. 55mPaㆍs M.W.543 |
Liquid type. Good dispersibility/solubility in adhesives, coatings, latexes, etc. |
AO-26 | Blend | Brown liquid Vis. 5,000mPaㆍs |
Excellent long-term heat stability. Low interference with crosslinking agent. For cross-linked PE and adhesives, etc |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
A-611 A-611RG |
AO-60/2112=1/1 | White powder (RG: granule) |
Mixture of ADK STAB AO-60 and ADK STAB 2112 Protects polymers effectively against thermal degradation during/after processing. Provides long-term heat stabilization for the life time of the article due to the synergistic effect of phenolic antioxidant and phosphite. |
A-612 A-612RG |
AO-60/2112=1/2 | White powder (RG: granule) |
Mixture of ADK STAB AO-60 and ADK STAB 2112 Protects polymers effectively against thermal degradation during/after processing. Provides long-term heat stabilization for the life time of the article due to the synergistic effect of phenolic antioxidant and phosphite. |
A-613 A-613RG |
AO-60/2112=1/3 | White powder (RG: granule) |
Mixture of ADK STAB AO-60 and ADK STAB 2112 Protects polymers effectively against thermal degradation during/after processing. Provides long-term heat stabilization for the life time of the article due to the synergistic effect of phenolic antioxidant and phosphite. |
A-512 A-512RG |
AO-50/2112=1/2 | White powder (RG: granule) |
Mixture of ADK STAB AO-50 and ADK STAB 2112. Protects polymers effectively against thermal degradation during / after processing. |
A-541 | AO-50/2112=4/1 | White powder |
Mixture of ADK STAB AO-50 and ADK STAB 2112. Protects polymers effectively against thermal degradation during / after processing. |
A-514 | AO-50/2112=1/4 | White powder |
Mixture of ADK STAB AO-50 and ADK STAB 2112. Protects polymers effectively against thermal degradation during / after processing. |
AO-18 | Blend | White powder M.P.>210℃ |
Provides long-term heat stabilization for filled/cross-linked polyolefins. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
CDA-100K | 36411-52-6 | White powder M.P.315-325℃ M.W.204 |
Show excellent copper deactivation. High heat stability. For polyolefins with fillers |
CDA-1M | Blend 36411-52-6 (main component) |
White powder M.P.>214℃ |
Higher dispersion and compatibility than CDA-100K. |
CDA-6S | 63245-38-5 | White powder M.P.211-217℃ M.W.498 |
Show excellent copper deactivation. Low volatility |
CDA-10 | 32687-78-8 | White powder M.P.224-229℃ M.W.553 |
Show antioxidant performance as it contains phenolic structure. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
AS-300 series | Blend | Pale yellow pellet M.P. 85-100℃ |
Can be readily used finished products by extrusion and injection molding. Suitable for Polyolefins, Polyesters, stylenic copolymers such as ABS, PC/ABS and HIPS. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
NA-11 | 85209-91-2 | White powder M.P.>400℃ M.W. 508 |
Effectively improves stiffness, heat distortion temperature, crystallization temperature/rate and clarity of PP. High resistance to heat and extraction. Odorless. |
NA-27 | Blend | White powder M.P.>230℃ |
Effectively improves stiffness, heat distortion temperature, crystallization temperature/rate and clarity of PP. Higher performance than NA-11 with better dispersion. |
NA-901 | Blend | White powder M.P.>210℃ |
Highly cost-effective. For Polyolefins. Conditions of FDA: B through H |
NA-902 | Blend | White powder M.P.>210℃ |
Highly cost-effective. For Polyolefins. Conditions of FDA: A through H |
NA-960 | Blend | White powder M.P.>200℃ |
It shows better dispersion regardless of kinds of neutralizer. Effectively improves stiffness, heat distortion temperature, crystallization temperature of PP. |
NA-21 | Blend 151841-65-5 (main component) |
White powder M.P.>210℃ |
Improves both transparency and mechanical properties effectively. Superior performance, even at lower loading level, compared to conventional clarifiers. Odorless. For Polyolefins. |
NA-71 | Blend | White powder M.P.>210℃ |
Improves both transparency and mechanical properties effectively. Superior performance, even at lower loading level, compared to conventional clarifiers. Odorless. For Polyolefins. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
FC-113 | Blend 25767-47-9 (main component) |
White powder Softening point 100-125℃ |
Provide excellent lubiricity for ABS with flame retardancy. |
AX-71 | 39471-52-8 | Light amber flake M.P. 68-75℃ M.W. 490 |
Excellent lubricant and ester exchange inhibitor for EVA, TPE & Others. Catalyst-deactivator for Polyesters. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
LA-24 | 70321-86-7 | Pale yellow powder M.P.139-142℃ M.W.447 |
Excellent thermal stability and low volatility, compared to other benzotriazol-type UVAs. |
LA-29 | 3147-75-9 | Pale yellow powder M.P.102-106℃ M.W.323 |
Less initial coloration. Low volatility. Good compatibility with many polymers. |
LA-300K | 103597-45-1 | Light yellow powder (RG: granule) M.P.194-200℃ M.W.659 |
Very low volatility due to high M.W. Excellent thermal stability. Excellent long term retention in the polymer. For engineering plastics requiring high processing temperatures. |
LA-32 | 2440-22-4 | Pale yellow powder M.P.127-132℃ M.W.225 |
Strong UV absorbe. Less initial coloration. For PVC, PS, PU, Acrylic polymers,elastomers, etc. |
LA-36 | 3896-11-5 | Pale yellow powder M.P.138-141℃ M.W.315 |
Common benzotriazole-type UVA. Excellent absorption in longerwavelength. UV regions, compared to other benzotriazole-type UVAs. |
LA-46 | 371146-04-02 | Light yellow powder M.P.106-108℃ M.W.512 |
High absorption from 280nm to 300nm wavelength. Excellent thermal stability and discoloration resistance against heat. Low volatility. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
LA-52 | 91788-83-9 | Pale yellow powder M.P.>65℃ M.W.847 |
Low basic N-CH3-type HALS with high amine content. Provides excellent light/heat stability especially to filled/pigmented polymers. |
LA-57 | 64022-61-3 | Pale yellow powder M.P.125-135℃ M.W.791 |
N-H-type HALS with high amine content. Provides excellent light stability to many polymers. |
LA-63P/FL | 101357-36-2, 85631-00-1 | Pale yellow powder M.P.85-105℃ M.W. approx.2,000 |
High molecular weight HALS. Very low volatility. Excellent resistance to extraction. Provides excellent light stability to thin applications, such as olefin films and engineering plastics which require high processing temperature. |
LA-68 | 101357-37-3, 85631-01-2 | Pale yellow powder M.P.80-110℃ M.W. approx.1,900 |
High molecular weight HALS. Very low volatility. Excellent resistance to extraction. Provides excellent light stability to thin applications, such as olefin films and engineering plastics which require high processing temperature. |
LA-72 | 41556-26-7 (main component |
Light yellow liquid SG. 0.99 Vis. (20℃)400mPaㆍs |
Liquid HALS. Main component is N-CH3-type HALS. Good dispersibility/solubility in coatings,sealants, etc. |
LA-77 | 52829-07-9 | White powder (G: granule) M.P.82-87℃ M.W.481 |
Low molecular weight N-H-type HALS. Provides excellent light stability to polymer molded articles, etc. |
LA-81 | 705257-84-7 | Light yellow liquid SG 0.95 Vis. 1,600mPaㆍs M.W.681 |
Very low basic NO-Alkyl-type HALS. Provides excellent light stability to lowpolar polymers, such as polyolefins, etc. Particularly for applications exposed to acid compounds such as agrochemicals. |
LA-82 | 68548-08-3 | Clear liquid Vis. 12mPaㆍs M.W.239 |
Polymerizable HALS having metacrylate group. Copolymerizable with a variety of monomers. |
LA-402XP/AF | Blend 167078-06-0 (main component) |
Light yellow pellet Softening point>120℃ |
Light stabilizer system PP masterbatch. Designed for use in pigmented polyolefins. Excellent compatibility with polyolefins. For PP/TPE automotive parts. |
LA-502XP | Blend | Light yellow pellet Softening point>120℃ |
Light stabilizer system PP masterbatch. Designed for use in pigmented polyolefins. Main component is LA-52. For PP/TPE automotive parts. |
LA-40MP/Si | 167078-06-0 (main component) |
White to pale yellow pellet (Si : Off-white powder) Softening point>120℃ |
Provides excellent light stability for PP automotive parts. Excellent compatibility with polyolefins and high resistance to blooming. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
FP-600 | 5945-33-5,181028-79-5 | Colorless viscous liquid SG1.26 Vis.(70℃)120-220mPaㆍs |
Halogen-free liquid type oligomeric phosphate flame retardant for engineering plastics. Hydrolysis stability, thermal stability and low volatility. |
PFR | 125997-21-9 | Colorless viscous liquid SG1.30 Vis.500-800mPaㆍs |
Halogen-free liquid type oligomeric phosphate flame retardant for engineering plastics. High phosphorus content and low volatility. |
FP-900L | 1003300-73-9 | Colorless or pale yellow viscous liquid SG1.30 Vis. (70℃)260-450mPaㆍs |
Halogen-free and environment-friendly (bisphenol-A free) liquid type oligomeric phosphate flame retardant for engineering plastics. Excellent thermal stability and low volatility compared to FP-600. Maintain physical and mechanical properties of polymers such as HDT compared to FP-600 |
FP-2100JC | Blend | White powder |
Halogen-free intumescent flame retardant for polyolefins,TPE, etc. Less effect on mechanical properties and density compared with metal hydroxides. Generates almost no smoke and CO during combustion. Higher heat stability than FP-2500S. |
FP-2500S | Blend | White powder |
Less dust type |
FP-2600U | Blend | White powder |
Halogen-free intumescent flame retardant for TPU. Less effect on mechanical properties and density compared with metal hydroxides. Generates almost no smoke and CO during combustion. Suppression of dripping and higher flame retardancy compared with conventional intumescent flame retardants. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
LX-803A | Blend 90498-90-1 (main component) |
White suspension |
Non-staining AO for rubber latex. Improving stain and color. Excellent stability for NOx gas. |
ADK STAB | CAS NO | Properties | Characteristics and applications |
---|---|---|---|
BF-1000 | Epoxidized 1,2-polybutadiene | Colorless liquid SG (30℃) 0.96 Vis.(45℃) 15,000-50,000mPaㆍs M.W. approx.1000 |
High adhesiveness due to epoxy group and vinyl group. Show compatibility for polymer blend and long-term heat stability. |
D-32 | Epoxidized octyl stearate | Colorless liquid SG (30℃) 0.915 Vis.52mPaㆍs |
Provide excellent long-term heat stability and color stability for polyolefins. |
Contact Us
아데카코리아㈜ 사업자등록번호 _ 402-81-14276 대표자 _ TAKAHASHI SHIN 개인정보보호책임자 _ 장현제
서울사무소 _ 서울특별시 중구 소공로 116(소공동, 서울센타빌딩)
본사 및 전주공장 _ 전라북도 완주군 봉동읍 완주산단2로 70
전주2공장 _ 전라북도 완주군 봉동읍 완주산단7로 20
수원연구소 _ 경기도 수원시 영통구 신원로 306(원천동, 외2 필지 영통이노플레스 1단지 1동 207, 208)