Photosensitive Materials
Adeka Korea supports the porduction of the best products with advanced technology.
- General Purpose Coatings/Casting Resins
- Photo/Thermal Curing Adhesives ADEKA Optomer KS Series
- Delayed Curing Adhesives DL Series
- Thermal Curing Resins ADEKA Opton KT Series
- Functional Hard Coatings
Surface Coating ADEKA OTOMER KR Series
| Product | SPEC | Features | Remark |
|---|---|---|---|
| KR-401 | Viscosity mPa 25℃ (70~160 mPa·s) Coating thickness(5~10㎛) irradiatio (UV irradiation 100~500mJ/㎠) |
General purpose type | Top varnishes for metals |
| KR-508 | Viscosity mPa 25℃ 150~290 Top Top varnishes for polyethylene |
Flexible type | Top varnishes for polyethylene |
| KR-567 | Viscosity mPa 25℃ 250~400 Coating thickness 5~10㎛ UV irradiation (UV irradiation 100~500mJ/㎠) |
Hard type | Top varnishes for Plastic films |
Resins for Optical lens kr KRX Series
| Product | SPEC | Features | Recommended curing condition |
|---|---|---|---|
| KRX-690-1 | Viscosity mPa 25℃ (200~500 mPa·s) Refractive Index (1.514/D) (Tg)123℃ |
Lens Low Refractive Index Type | Coating thickness 0.1~2mm UV irradiation 5000~10000mJ/㎠ |
| KRX-690-5 | Viscosity mPa 25℃ (3500~5500 mPa·s) Refractive Index (1.572/D) (Tg) 183℃ |
Lens High Refractive Index type | |
| KRX-695A | Viscosity mPa 25℃ (200~500 mPa·s) Refractive Index (1.514/D) (Tg) 114℃ |
For casting Thick cure type |
Optical Shape Transcription Resin KR-Series
| Product | SPEC Viscosity / Viscosity mPa 25℃ |
Features Main applications |
|---|---|---|
| KR-773 | Refractive Index 1.51~1.59(D) (Tg)30~140℃ Viscosity mPa 25℃ (250~3000 mPa·s) |
For Lenticular lens, Fresnel lens, Prism Sheet etc. |
Photo/Thermal Curing Adhesives ADEKA Optomer KS Series
| Product | SPEC (Spec)Viscosity | Characteristic | Remark Recommended curing condition |
|---|---|---|---|
| KS-800 | Viscosity mPa 25℃ 70~150 | Low viscosity | Coating Thickness 5~50㎛ Curing UV500~1000mJ/㎠ + Heat 130℃ X 15min (or 150℃ X 5min) Coating Thickness 5~10㎛ 5000~1000mJ/㎠ |
| KS-820 | Viscosity mPa 25℃ (2000~9000 mPa·s) | High Viscosity | |
| KS-823-5 | Viscosity mPa 25℃ ((100000~200000 mPa·s) (Thixotropy ratio 5~10) |
High, heat resistance High Thixotropy |
Delayed Curing adhesives DL Series
| Product | SPEC (Spec) Viscosity Viscosity mPa 25℃ Hardened product properties Properties of cured film |
Characteristic | Remark Hardening condition example Typical Curing condition |
|---|---|---|---|
| DL-100 | 00 Viscosity mPa 25℃ (2000~4000 mPa·s) (Tg) 35℃ Shrinkage on Curing 3.7% |
Flexible | Thickness 10~100㎛ UV :50~100mJ/㎠ |
| DL-200 | Viscosity mPa 25℃ (2000~4000 mPa·s) Tg 107℃ Shrinkage on Curing 4.0% |
Hard | Thickness 10~100㎛ UV :50~100mJ/㎠ |
Thermal Curing Resins ADEKA OPTON KT Series
| Product | Type Viscosity Viscosity mPa 25℃ Recommended curing condition Recommended curing condition |
Characteristic | Remark |
|---|---|---|---|
| KT-960 | Viscosity mPa 25℃ (150~550 mPa·s) | Low viscosity | Adhesives, Inks |
| KT-980 | 2000~10000 | High viscosity | - |
Hard Coatings for optical use ADEKA OPTOMER HC Series
| Product | Materials Main application Solid content (solvent) solid content (solvent) Viscosity Viscosity mPa 25℃ Hardened product properties Properties of cured film |
Characteristic | Remark Recommended curing condition |
|---|---|---|---|
| HC-211 | PET Film TAC Film 50% (PGM/MEK) 3~7 Pensil hardness 2H Refractive index 1.52> PET Film TAC Film 40% (PGM/MEK) 1~5 Pensil hardness 3H Refractive index 1.52 Refractive index PET Film TAC Film 50% (PGM/Propyl Acetate) 3~7 Pensil hardness 4H Refractive index 1.53 |
Standard | UV:100㎛ Easy adhesion Pet Flim, 80㎛ TACFlim Thickness : 5~10㎛ Drying 80℃ X 1m UV : 100~300mJ/㎠ Base film 100㎛ PET Film , or 80㎛ TAC film Thickness 5~10um Drying 80℃ X 1min UV :100~300mJ/㎠ |
| HC-504 | sratch resistan/Containing colloidal silica | ||
| HC-206 | Hard |
Highly stretchable coatings HC Series
| Product | SPEC | Features | Recommended curing condition |
|---|---|---|---|
| HC-201-38 | PET Film TAC Film PMMA Film , PC film 40%(PGM/MEK) 30~50 Pensil hardness (H~ 2H) Stretch rate (%) 10 |
Hard (Containing colloidal silica) | Thickness : 5~10㎛ Drying 80℃ X 1 min. UV : 300~1000mJ/㎠ Thickness 5~10㎛ Drying 80℃ X 1min UV :300~1000mJ/㎠ |
| HC-201-46 | PET Film TAC Film PMMA Film , PC film 40% (PGM/MEK) 30~50 Pensil hardness F~H Refractive index (%) 40~50 |
Highly Stretchable |
High refractive index hard coatings ADEKA OPTOMER RF Series
| Product | SPEC | Features | Remark Recommended curing condition |
|---|---|---|---|
| RF-102 | 70%(MZBK) Pensil hardness F Refractive index 1.62 |
Non-inorganic filler | UV :100㎛ Easy adhesion PET flim Thickness :5~10㎛ Drying 80℃ X 1m uv:500mJ/㎠ |